The role of service-induced residual stresses in initiating and propagating stress corrosion cracking (SCC) in a 316 stainless steel pressure-relief-valve nozzle set-Reference-Cited by-同舟云学术

The role of service-induced residual stresses in initiating and propagating stress corrosion cracking (SCC) in a 316 stainless steel pressure-relief-valve nozzle set

Published:2019-11 Issue: Volume:105 Page:1229-1251
ISSN:1350-6307
Container-title:Engineering Failure Analysis
language:en
Short-container-title:Engineering Failure Analysis

Author:

Abdul Jawwad Abdul Kareem,Mahdi Mofid,Alshabatat Nabeel

Funder

ACUREN

Publisher

Elsevier BV

Subject

General Engineering,General Materials Science

Reference15 articles.

1. Stress corrosion cracking in 316L stainless steel bellows of a pressure safety valve;Panda;Eng. Fail. Anal.,2014

2. Role of residual stresses induced by industrial fabrication on stress corrosion cracking susceptibility of austenitic stainless steel;Ghosh;Mater. Des.,2011

3. Stress corrosion cracking at low loads: surface slip and crystallographic analysis;Zhu;Corros. Sci.,2015

4. Failure analysis and prevention in SCC and corrosion fatigue cases;Komai;Int. J. Fatigue,1998

5. Some observations on the current status in the understanding of stress-corrosion cracking of stainless steels;Trethewey;Mater. Des.,2008

Cited by 10 articles. 订阅此论文施引文献订阅此论文施引文献，注册后可以免费订阅5篇论文的施引文献，订阅后可以查看论文全部施引文献

1. Multiscale Residual Stress Evaluation of Engineering Materials/Components Based on Neutron and Synchrotron Radiation Technology;ACTA METALL SIN;2023

2. Effects of non-symmetric non-uniformly distributed welding residual stress on fatigue failure initiation and propagation in a hydropower generator shaft;Multidiscipline Modeling in Materials and Structures;2023-06-30

3. Research progress in stress corrosion of additively manufactured 316L stainlesss teels;CAILIAO GONGCHENG;2023

4. The Failure Mechanism of the 316 SS Heat Exchanger Tube in the Geothermal Water Environment;Materials;2022-11-16

5. Thermo-mechanical stress analysis of feed-water valves in nuclear power plants;Nuclear Engineering and Technology;2021-09