Osteoconductivity of bioactive Ti-6Al-4V implants with lattice-shaped interconnected large pores fabricated by electron beam melting

Abstract

Additive manufacturing has facilitated the fabrication of orthopedic metal implants with interconnected pores. Recent reports have indicated that a pore size of 600 μm is beneficial for material-induced osteogenesis. However, the complete removal of the metal powder from such small pores of implants is extremely difficult especially in electron beam melting (EBM). We therefore developed a new type of Ti-6Al-4V implant with lattice-shaped interconnected pores measuring 880–1400 μm, which allowed for the easy removal of metal powder. This implant was fabricated by EBM and treated with NaOH, CaCl2, heat, and water (ACaHW treatment) to render the metal surface bioactivity. In the present study, the mechanical and chemical property of the implants and the biocompatibility were evaluated. The SEM and micro-CT images demonstrated the 3D interconnectivity of the porous structures. The average porosity of the porous titanium implant was 57.5%. The implant showed maximum compressive load of 78.9 MPa and Young's modulus of 3.57 GPa which matches that of human cortical bone. ACaHW treatment of the porous Ti-6Al-4V implants induced apatite formation in simulated body fluid in vitro. The ACaHW-treated porous implants harvested from rabbit femoral bone showed direct bonding of bone to the metal surface without interposition of fibrous tissue. The porous ACaHW-treated implant had a higher affinity to the bone than the untreated one. The mechanical strength of implant fixation assessed using the push-out test was significantly higher in the ACaHW-treated implant than in untreated one. FE-SEM analysis and EDX mapping after push-out test of solid implants showed a lot of bone tissue patches on the surface of the ACaHW-treated implant. These results suggest that the new ACaHW-treated Ti-6Al-4V implant with lattice-shaped interconnected pores is a superior alternative to conventional materials for medical application.