1. Gangneung-Wonju National University
Abstract
Recrystallization kinetics of Mg alloy has been investigated in this study. Mg alloys such as Mg-3Al and Mg-6Al in weight percents were cast into rectangular shaped ingots of 20mm thickness. Solution treatment at 400°C for 24 hrs has been carried out on these ingots and pure Mg for comparison. Heat treated ingots including pure Mg were rolled at room temperature by thickness reductions of 10, 20, and 30 percents. Annealing treatment for recrystallization has been conducted on these cold-rolled plates at temperatures of 200, 300, and 400°C for various times from 1 min to 24 hrs. The microstructure observation and hardness measurement conducted on the recrystallized specimens revealed that static recrystallization at 200°C was very slow and expedited with increasing temperature, regardless of Al contents. While recrystallization behavior of Mg at 300°C appeared to be retarded by increase in Al contents, that of Mg was not affected at 400°C.
Publisher
Trans Tech Publications, Ltd.
Subject
Mechanical Engineering,Mechanics of Materials,Condensed Matter Physics,General Materials Science
Reference5 articles.
1. W. Qiu, E-H. Han, L. Liu: Trans. Nonferrous Met. Soc. China Vol. 20 (2010), pp.481-487.
2. S.M. Masoudpanah, R. Mahmudi: Mater. Sci. & Eng. A, Vol. 526 (2009), pp.22-30.
3. Y. Wang, S. Guan, X. Zeng, W. Ding: Mater. Sci. & Eng. A, Vol. 416 (2006), pp.109-118. 12hr 40min 40min.
4. M.R. Barnett, M.D. Nave, C.J. Bettles: Mater. Sci. & Eng. A, Vol. 386 (2004), pp.205-211.
5. N. -J. Park, S. -H. Han: Kor. J. Met. Mater. Vol. 48 (2010), pp.498-505.
Cited by
3 articles.
订阅此论文施引文献
订阅此论文施引文献,注册后可以免费订阅5篇论文的施引文献,订阅后可以查看论文全部施引文献