Effect of Sintering Aids Sorts on Properties of Prepared Al2O3-Al Cermet

Abstract

Cermet while maintaining the excellent properties of ceramic materials, but also have the advantages of a metal material, is an important new engineering materials. In this paper, Al-Al2O3 cermet is prepared adding different sintering aids via the powder metallurgy method to study the properties of Al-Al2O3 cermet. The conclusions are shown the adding sintering aids can significantly improve the sintered density of Al-Al2O3 cermet. The sintering aiding effect of adding MgO is better than that of SiO2 and Y2O3, and the hardness and the strength of the sample are higher than those of samples with SiO2 and Y2O3, and the densification degree of Al-Al2O3 metal ceramic material is the best, the relative density is 94.8%, the surface hardness is 824HV. The flatness of the surface of the sample adding MgO shows that the bonding strength between aluminum powder and alumina powder is high. The prepared Al-Al2O3 cermet adding different sintering aids have higher density and fewer pores in the microstructure the prepared Al-Al2O3 cermet adding sintering aids has a package structure.