The influence of operation of API 5L X67 steel and specimen notch orientation on the impact toughness
-
Published:2025-04-30
Issue:2
Volume:61
Page:111-117
-
ISSN:3041-1815
-
Container-title:Physicochemical Mechanics of Materials
-
language:
-
Short-container-title:PCMM
Author:
, Demianchuk D. O., Tsyrulnyk O. T.ORCID, , Solovei P. R., , Nykyforchyn H. M.ORCID, , Zvirko О. І.ORCID,
Abstract
The operational embrittlement based on the determination of the impact toughness KCV of longitudinal and transverse to the rolling direction specimens of API 5L X67 steel of the reserve pipes and operated for 34 years on the gas main pipeline was investigated. The influence of different orientations of the notch in the specimens relative to the rolling direction and the pipe axis was analyzed and a significant influence of this factor on the impact toughness was revealed, which is generally higher for specimens with a notch oriented in the short transversal direction. The sensitivity of KCV to operational degradation was the highest for tests of transverse specimens with a concentrator in the axial direction. Using macrofractographic analysis, a typical low-energy delamination along the rolling direction was observed.
Publisher
National Academy of Sciences of Ukraine (Co. LTD Ukrinformnauka) (Publications)
Reference21 articles.
1. 1. R. Hrabovskyy, Y. Kryzhanivskyy, O. Tuts, O. Mandruk, V. Tyrlych, V. Artym, and Y. Sapuzhak, "Impact of long-term operation on reliability and durability of natural gas pipeline: potential environmental consequences of accidents," Procedia Structural Integrity, 59, 112-119 (2024). 2. 2. P. Martin, I. B. Ocko, S. Esquivel-Elizondo, R. Kupers, D. Cebon, T. Baxter, and S. P. Hamburg, "A review of challenges with using the natural gas system for hydrogen," Energy Sci. Eng., 12, Is. 10, 3995-4009 (2024). 3. 3. H. Nykyforchyn, L. Unigovskyi, O. Zvirko, O. Tsyrulnyk, and H. Krechkovska, "Pipeline durability and integrity issues at hydrogen transport via natural gas distribution network," Procedia Structural Integrity, 33, 646-651 (2021). 4. 4. O. Zvirko, H. Nykyforchyn, H. Krechkovska, O. Tsyrulnyk, M. Hredil, O. Venhryniuk, and I. Tsybailo, "Evaluating hydrogen embrittlement susceptibility of operated natural gas pipeline steel intended for hydrogen service," Eng. Fail. Anal., 163, Part A. (2024). Article number 108472. 5. 5. L. Nyrkova, S. Osadchuk, Y. Kharchenko, L. Goncharenko, A. Klymenko, V. Kostin, and A. Rybakov, "Comparative studies of stress-corrosion cracking of long-term exploited and storage pipes of X70 steel of main gas pipeline," Mech. Tech. Struct. Mater., 60, 237-246 (2023).
|
|