Abstract
Abstract
The critical chloride threshold is a key parameter in the service life design of reinforced concrete structures exposed to chloride-bearing environments. This paper investigates the role of concrete composition, and particularly the effect of supplementary cementing materials, on the chloride threshold. To simulate real exposure conditions, ponding tests were carried out on reinforced concrete specimens with bars in free corrosion conditions and corrosion initiation was detected through corrosion potential and corrosion rate measurements. After two and a half years, the ponding was followed by an ageing period and the initiation of corrosion was further detected with anodic potentiostatic polarisation tests. Results of the tests showed several limitations of the approach based on chloride penetration and monitoring of free corrosion parameters to investigate the chloride threshold. In spite of this, a possible role of natural pozzolan and coal fly ash additions in leading to higher values of the chloride threshold and ground limestone in promoting lower values of the chloride threshold could be observed.
Publisher
Springer Science and Business Media LLC
Subject
Mechanics of Materials,General Materials Science,Building and Construction,Civil and Structural Engineering
Reference57 articles.
1. Alonso C, González JA (1978) Quantitative measurements of corrosion rate of reinforcing steels embedded in concrete using polarization resistance measurements. Mater Corr 29(8):515–519. doi:10.1002/maco.19780290804
2. Alonso C, Andrade C, Castellote M, Castro P (2000) Chloride threshold values to depassivate reinforcing bars embedded in a standardised OPC mortar. Cement Concrete Res 30(7):1047–1055. doi:10.1016/S0008-8846(00)00265-9
3. Alonso C, Castellote M, Andrade C (2002) Chloride threshold dependence of pitting potential of reinforcements. Electrochim Acta 47(21):3469–3481. doi:10.1016/S0013-4686(02)00283-9
4. Alonso MC, Sanchez M (2009) Analysis of the variability of chloride threshold values in the literature. Mater Corros 60(8):631–637. doi:10.1002/maco.200905296
5. Andrade C (2003) Determination of the chloride threshold in concrete. In: Cigna R, Andrade C, Nürnberger U, Polder R, Weydert R, Seitz E (eds), Corrosion of steel in reinforced concrete structures, Luxembourg: COST 521, Final Report, pp 101–111
Cited by
34 articles.
订阅此论文施引文献
订阅此论文施引文献，注册后可以免费订阅5篇论文的施引文献，订阅后可以查看论文全部施引文献