LIGNOCELLULOSIC LINERS BASED ON WOOD WOOL

Abstract

Basic physical and mechanical properties of lignocellulosic liners up to 1.5 mm thick with a compact and non-crumbling surface based on wood wool and thermoplastic water based glues were determined. PVAc and starch glue with a high proportion of water content were used. The dry mat was pressed gradually under high pressure up to 28 MPa and a temperature of around 190°C with the release of steam. Tests according to the CEPI (Confederation of European Paper Industries) standards were adopted. Procedures for tensile strength according to ISO 1924-2 (2008), Burst strength according to ISO 2758 (2014), puncture according to ASTM D781-68 (1973), water absorption according to ISO 5637 (1989) and porosity according to TAPPI Test method T460 were applied.