Experimental study of a 3D-printing technique combined with biphasic calcium phosphates to treat osteonecrosis of the femoral head in a canine model

Abstract

Abstract Objective This study was aimed to use a digital design of 3D-printing technology to create a surgical navigation template. At the same time, biphasic calcium phosphate (BCP) was applied to treat osteonecrosis of the femoral head (ONFH) in animal models, based on accurate positioning of necrotic lesions in the navigation templates and observation of its therapeutic effect. Methods Fifteen healthy adult male and female beagle dogs weighing 20 + 2 kg were randomly divided into three groups (n = 5) after establishing a model of ONFH using the liquid nitrogen freezing method. Each model underwent necrotic lesion creation and BPC implantations on one side of the femoral head and only necrotic lesion creation on the other side of the femoral head. Each group underwent CT examination, gross observation, histological examination and immunohistochemical staining at 6 weeks, 12 weeks and 18 weeks postoperatively. Results At weeks 6, 12, and 18, CT and gross examination showed that the necrotic area in the experimental group was basically intact and had been completely raised by BCP material. In the control group, there were signs of bone repair in the femoral head, but there were still large bone defects and cavities. At week 18, extensive collapse of the cartilage surface was observed. Through histological examination, in the experimental group at 12 and 18 weeks, a large number of new and reconstructed bone trabeculae containing a large amount of collagen fibres were observed (P < 0.05), while in the control group, there was extensive necrosis of the bone trabeculae without cellular structural areas. Immunohistochemical examination observation: A large number of CD31-positive cells were observed in the experimental group at 6 weeks, gradually decreasing at 12 and 18 weeks (P < 0.05), while a small number of CD31-positive cells were observed in the control group at 18 weeks. Conclusion The 3D-printed navigation template can accurately locate ONFH lesions. Implantation of BCP material can effectively play a supporting role, prevent the collapse of the loading surface, and induce bone formation and angiogenesis to some extent.