Effect of Aging Time and Temperature on Microstructure and Mechanical Properties of AA7075 Alloy

Author:

BUDAK Selahattin1ORCID,ÇOLAK Harun2ORCID,YAKUT Yusuf2

Affiliation:

1. GÜMÜŞHANE ÜNİVERSİTESİ, MÜHENDİSLİK VE DOĞA BİLİMLERİ FAKÜLTESİ, MAKİNE MÜHENDİSLİĞİ BÖLÜMÜ

2. ONDOKUZ MAYIS ÜNİVERSİTESİ, YEŞİLYURT DEMİR ÇELİK MESLEK YÜKSEKOKULU, MAKİNE VE METAL TEKNOLOJİLERİ BÖLÜMÜ

Abstract

In this study, the effect of aging at different temperatures and times on the microstructure and mechanical properties of AA7075-T6 alloy was investigated. The samples prepared for the experimental studies were subjected to solution, quenching, and then aging heat treatment at 100 ⁰C and 200 ⁰C for different periods (42-66-90 hours). The microstructure and mechanical properties of the experimental samples were investigated by hardness, compression test and scanning electron microscope (SEM). As a result of the studies, it was determined that the aging heat treatment had a positive effect on the microstructure and mechanical properties of the AA7075 alloy compared to the reference sample. Especially as a result of the heat treatments at 100 ⁰C, higher results were obtained in hardness and compression strength compared to the initial values.

Publisher

Gumushane University Journal of Science and Technology Institute

Subject

General Engineering

Reference22 articles.

1. Ak, M. (2012). AA206 alüminyum döküm alaşımında empürite demirin mekanik özelliklere etkilerinin incelenmesi [Yüksek Lisans Tezi, İstanbul Teknik Üniversitesi Fen Bilimleri Enstitüsü].

2. Aydın, B. (2002). AA2014 Alaşımında Yaşlandırma Isıl İşleminin İşlenebilirlik Üzerindeki Etkilerinin İncelenmesi [Yüksek Lisans Tezi, Gazi Üniversitesi Fen Bilimleri Enstitüsü]

3. Baydoğan, M., Çimenoğlu, H., & Kayali, E. S. (2004). RRA işleminin 7075 alaşımının mekanik özelliklerine etkisi. İtüdergisi/d, 3(6), 108-116.

4. Budak, S. (2016). Alüminyum silisyum alaşımı bir yatak malzemesinin aşınma performansına kolemanit ilavesinin etkisinin incelenmesi/Investigation of effect of colemanite addition on the wear performance of an aluminum silicon alloy journal bearing material [Doktora Tezi, Fırat Üniversitesi Fen Bilimleri Enstitüsü].

5. Chen, J., Zhen, L., Yang, S., Shao, W., & Dai, S. (2009). Investigation of precipitation behavior and related hardening in AA 7055 aluminum alloy. Materials Science and Engineering: A, 500(1-2), 34-42. https://doi.org/10.1016/j.msea.2008.09.065

同舟云学术

1.学者识别学者识别

2.学术分析学术分析

3.人才评估人才评估

"同舟云学术"是以全球学者为主线,采集、加工和组织学术论文而形成的新型学术文献查询和分析系统,可以对全球学者进行文献检索和人才价值评估。用户可以通过关注某些学科领域的顶尖人物而持续追踪该领域的学科进展和研究前沿。经过近期的数据扩容,当前同舟云学术共收录了国内外主流学术期刊6万余种,收集的期刊论文及会议论文总量共计约1.5亿篇,并以每天添加12000余篇中外论文的速度递增。我们也可以为用户提供个性化、定制化的学者数据。欢迎来电咨询!咨询电话:010-8811{复制后删除}0370

www.globalauthorid.com

TOP

Copyright © 2019-2024 北京同舟云网络信息技术有限公司
京公网安备11010802033243号  京ICP备18003416号-3