PREPARATION AND CHARACTERISATION OF ZnO THIN FILMS DEPOSITED BY RF SPUTTERING METHOD-Reference-Cited by-同舟云学术

PREPARATION AND CHARACTERISATION OF ZnO THIN FILMS DEPOSITED BY RF SPUTTERING METHOD

Published:2024-02-07 Issue:6 Volume:7 Page:329-338
ISSN:2616-1370
Container-title:FUDMA JOURNAL OF SCIENCES
language:
Short-container-title:FJS

Author:

Abdullahi Bilyaminu,Abdullahi S.,Abdullahi M. B.,Wara A. M.

Abstract

Zinc oxide (ZnO) thin films deposited on corning glass substrates at 100ºC substrate temperature by radio frequency deposition were annealed the open air and icrowave oven at 150ºC. The influence of open-air annealing (OAA) and microwave annealing (MWA) were studied. The results obtained showed that MWA annealing can improve not only the crystal but also the optical properties of the ZnO thin films. A high transmittance is obtained in all the annealed samples (S1, S2, S4 and S5) demonstrating >90% at 650 nm wavelength. Reflectance in all the samples was < 29% with a minimum standing at 23.78% as recorded for sample S5. The band gap for the annealed samples (S1, S2, S4 and S5) was determined at 3.26 eV, 3.32 eV, 3.29 eV and 3.34 eV respectively. Absorption coefficient stood at 0.0225 cm-1, 0.0179 cm-1, 0.0180 cm-1, 0.0186 cm-1 and 0.0181 cm-1 for the as-deposited sample and the respectively. The optical and structural properties analysis showed that OAA and MWA annealing at suitable temperatures considered can significantly improve some properties of the ZnO thin films making the films suitable for applications in optoelectronics and photovoltaics.

Publisher

Federal University Dutsin-Ma

Reference11 articles.

1. Abdullahi, S., & Maiyama, B. A. (2017). The Role of Air Annealing on the Structural and Electrical Properties of Zinc Oxide (ZnO) Thin Film Deposited by Rf Sputtering Technique: Scholars. Journal of Engineering and Technology, 5(12), 704-708.

2. Abdullahi, S., Momoh, M., Moreh, A.U., Isah, K.U., & Argungu, G.M. (2015). Influence of Thickness on Optical Properties of ZnO Thin Films prepared by Radio Frequency Sputtering Technique. Nigerian Journal of Solar Energy, 26, 66-70.

3. Abdullahi, S., Momoh, M., Moreh, A.U., Bayawa, A. M., Hamza, B., Argungu, G.M., & Popoola, O. T. (2017). Influence of Annealing Temperature on Optical and Electrical Properties of Cu2ZnSnS4(CZTS) thin Films Deposited by Sputtering Method from a Single Quaternary Target. International Journal of Scientific Research in Science and Technology, 3(1), 77-82.

4. Abdullahi, S., Momoh, M., & Isah, K. U. (2014). Electrical and Structural Prop erties of Radio Frequency (RF) Sputtered ZnO Thin Film at Low Substrate Temperature. Journal of Electrical Engineering, vol 2, pp 12-19.

5. Al-ofin, H. H., Abdel-Raheem, M. M., Ateyyah., & Al-Baradi, M. (2012). Structural and optical properties of Al2ZnO4 thin films deposited by D.C. sputtering technique. Journal of non-oxide Glasses, 3(3¬), pp39 – 54.