Effect of fly ash and curing temperature on the properties of magnesium phosphate repair mortar

Abstract

AbstractThis article is aimed at discussing the combined effect of mineral admixture and servicing temperature, especially in cold environment, on the properties of magnesium phosphate repair mortar (MPM). The influence mechanism of fly ash content on the microstructure and performance of MPM were firstly investigated, and then the evolution rules in properties of fly ash modified MPM cured at − 20 °C, 0 °C, 20 °C and 40 °C were further revealed. The results show that the incorporation of fly ash has no significant effect on the setting time and fluidity of MPM. When MPM is modified with 10 wt% and 15 wt% fly ash, its mechanical properties, adhesive strength, water resistance, and volume stability are effectively improved. Fly ash reduces the crystallinity and continuity of struvite enriched in hardened MPM, and its particles are embedded among struvite and unreacted MgO. The compressive strength of MPM-10 cured for various ages increases with the elevating of curing temperature, while the flexural strength, interfacial bonding strength, strength retention and linear shrinkage exhibits the opposite laws. When cured at 0 °C and − 20 °C, MPM-10 still has good early strength, water resistance and interfacial bonding properties, which indicates that MPM-10 provides with an ability of emergency repair of cracked components served in cold environments.