Boosting carrier mobility and stability in indium–zinc–tin oxide thin-film transistors through controlled crystallization

Author:

On Nuri,Kim Bo Kyoung,Kim Yerin,Kim Eun Hyun,Lim Jun Hyung,Hosono Hideo,Kim Junghwan,Yang Hoichang,Jeong Jae Kyeong

Abstract

Abstract We investigated the effect of film thickness (geometrical confinement) on the structural evolution of sputtered indium-zinc-tin oxide (IZTO) films as high mobility n-channel semiconducting layers during post-treatment at different annealing temperatures ranging from 350 to 700 °C. Different thicknesses result in IZTO films containing versatile phases, such as amorphous, low-, and high-crystalline structures even after annealing at 700 °C. A 19-nm-thick IZTO film clearly showed a phase transformation from initially amorphous to polycrystalline bixbyite structures, while the ultra-thin film (5 nm) still maintained an amorphous phase. Transistors including amorphous and low crystalline IZTO films fabricated at 350 and 700 °C show reasonable carrier mobility (µFE) and on/off current ratio (ION/OFF) values of 22.4–35.9 cm2 V−1 s−1 and 1.0–4.0 × 108, respectively. However, their device instabilities against positive/negative gate bias stresses (PBS/NBS) are unacceptable, originating from unsaturated bonding and disordered sites in the metal oxide films. In contrast, the 19-nm-thick annealed IZTO films included highly-crystalline, 2D spherulitic crystallites and fewer grain boundaries. These films show the highest µFE value of 39.2 cm2 V−1 s−1 in the transistor as well as an excellent ION/OFF value of 9.7 × 108. Simultaneously, the PBS/NBS stability of the resulting transistor is significantly improved under the same stress condition. This promising superior performance is attributed to the crystallization-induced lattice ordering, as determined by highly-crystalline structures and the associated formation of discrete donor levels (~ 0.31 eV) below the conduction band edge.

Funder

Samsung Display

Publisher

Springer Science and Business Media LLC

Subject

Multidisciplinary

同舟云学术

1.学者识别学者识别

2.学术分析学术分析

3.人才评估人才评估

"同舟云学术"是以全球学者为主线,采集、加工和组织学术论文而形成的新型学术文献查询和分析系统,可以对全球学者进行文献检索和人才价值评估。用户可以通过关注某些学科领域的顶尖人物而持续追踪该领域的学科进展和研究前沿。经过近期的数据扩容,当前同舟云学术共收录了国内外主流学术期刊6万余种,收集的期刊论文及会议论文总量共计约1.5亿篇,并以每天添加12000余篇中外论文的速度递增。我们也可以为用户提供个性化、定制化的学者数据。欢迎来电咨询!咨询电话:010-8811{复制后删除}0370

www.globalauthorid.com

TOP

Copyright © 2019-2024 北京同舟云网络信息技术有限公司
京公网安备11010802033243号  京ICP备18003416号-3