Effect of Ceramic Thickness on the Bond Strength to Resin-Luting Agents before and after Thermal Cycling

Author:

Souza Carolina Rodrigues de1ORCID,Costa Ana Rosa2ORCID,Borges Lincoln Pires Silva1ORCID,Ferraz Analia Gabriella Borges1ORCID,consani Rafael Leonardo Xediek1ORCID,Pacheco Rafael Rocha3ORCID,Correr Américo Bortolazzo1ORCID,Correr-Sobrinho Lourenço1ORCID

Affiliation:

1. State University of Campinas, Brazil

2. State University of Campinas, Brazil; Universidade de Araras, Brazil

3. The Dental College of Georgia at Augusta University, USA

Abstract

Abstract This study investigated microshear bond strength (µSBS) of two (2) dual-cured resin-luting agents (RelyX™ Ultimate and RelyX™ U200) when photoactivated through varying thicknesses of lithium disilicate, with or without thermal cycling. Discs of IPS e.max Press of 0.5, 1.5, and 2 mm in thickness were obtained. Elastomer molds (3.0 mm in thickness) with four cylinder-shaped orifices 1.0 mm in diameter, were placed onto the ceramic surfaces and filled with resin-luting agents. A Mylar strip, glass plate, and load of 250 grams were placed over the filled mold. The load was removed and the resin-luting agents were photoactivated through the ceramics using a single-peak LED (Radii Plus.) All samples were stored in distilled water at 37oC for 24 h. Half of the samples were subjected to thermal cycling (3,000 cycles; 5ºC and 55ºC). All samples were then submitted to µSBS test using a universal testing machine (Instron 4411) at a crosshead speed of 0.5 mm/min. Data were submitted to three-way ANOVA and Tukey post-hoc test (α=0.05). The mean µSBS at 24 h was significantly higher than after thermal cycling (p<0.05). No statistical difference was found between resin-luting agents (p > 0.05). The mean µSBS for groups photoactivated through 0.5 mm ceramic were significantly higher than 1.5 mm and 2.0 mm (p < 0.05). In conclusion, increased ceramic thicknesses reduced the bond strength of tested resin-luting agents to lithium disilicate. No differences were found between resin-luting agents. Thermal cycling reduced the bond strength of both resin-luting agents.

Publisher

FapUNIFESP (SciELO)

Reference39 articles.

同舟云学术

1.学者识别学者识别

2.学术分析学术分析

3.人才评估人才评估

"同舟云学术"是以全球学者为主线,采集、加工和组织学术论文而形成的新型学术文献查询和分析系统,可以对全球学者进行文献检索和人才价值评估。用户可以通过关注某些学科领域的顶尖人物而持续追踪该领域的学科进展和研究前沿。经过近期的数据扩容,当前同舟云学术共收录了国内外主流学术期刊6万余种,收集的期刊论文及会议论文总量共计约1.5亿篇,并以每天添加12000余篇中外论文的速度递增。我们也可以为用户提供个性化、定制化的学者数据。欢迎来电咨询!咨询电话:010-8811{复制后删除}0370

www.globalauthorid.com

TOP

Copyright © 2019-2024 北京同舟云网络信息技术有限公司
京公网安备11010802033243号  京ICP备18003416号-3