Effect of Acetic Acid on Compressive Strength and Geometric Texture of the Surface of C20/25 Class Concrete

Abstract

Concrete is a highly alkaline material; therefore, the presence of organic acids (acetic, butyric, lactic) from agricultural sewage constitutes a threat to the concrete and the environment. The investigations were aimed at simulating the influence of highly concentrated organic acids on concrete elements of livestock buildings. Cubic samples 100 × 100 × 100 mm of the ordinary concrete were immersed in 10% acetic acid for 270 days. Then, the compressive strength and mass decrement of the samples were determined as well as using SEM images and a 3D-profilograph to profile the surface roughness and depth of changes evoked in the structure of the samples by penetrating acid. The results were compared with those for a control sample (not subjected to the effects of aggressive agents) as well as for samples placed in a neutral and alkaline environment. The compressive strength of the samples stored in the acidic environment was 22.23% lower than that of the control sample, whereas the compressive strength of those samples stored in an alkaline environment were 44.27% higher. Conclusions from these investigations can be of innovative importance in the preparation of environmental impact reports, which are necessary for obtaining permission for the construction and use of livestock buildings, and afterward in the reduction of the impact of these buildings on the environment and surface and underground water resources.