Abstract
In order to investigate the durability of two kinds of fiber-reinforced composite materials, and obtain the degradation mechanism and failure model in a hygrothermal environment, E-glass- fiber-reinforced composite materials, glass fiber-reinforced epoxy vinyl ester and glass fiber-reinforced unsaturated polyester (named GF/VE and GF/UP, respectively) were chosen to suffer rigorous hygrothermal aging. Their mechanical performance was monitored during the aging process to evaluate their durability. The cause of deterioration of the composite was comprehensively analyzed. Based on the analysis results of attenuated total-reflectance-Fourier-transform infrared spectroscopy (ATR-FTIR), thermogravimetric analysis (TGA) and dynamic mechanical analysis (DMA), the change mechanism of chain structure of the resin molecule was proposed. SEM (scanning electron microscopy), X-ray photoelectron spectroscopy (XPS) and X-ray diffraction (XRD) were used to analyze the microstructure and degradation mechanism of the fiber and the interface between fiber and matrix. The degradation mechanism of the composite system, including the resin, the fiber and the interface, was obtained, and it was found that the deterioration of the matrix resin caused by the hygrothermal environment was the main factor leading to the decline in composites performance.
Funder
State Administration of Science, Technology and Industry for National Defense