One-Year Evaluation of High-Power Rapid Curing on Dentin Bond Strength

Abstract

This study investigated the effect of 3 s light-curing with a high-power LED curing unit on the shear bond strength of bulk-fill composites. Four bulk-fill composites were bonded to dentin with a universal adhesive (Scotchbond Universal Plus): two materials designed for rapid curing (Tetric PowerFill and Tetric PowerFlow) and two controls (Filtek One Bulk Fill Restorative and SDR Plus Bulk Fill Flowable). The 4 mm composite layer was light-cured with Bluephase PowerCure for 20 s at 1000 mW/cm2 (“20 s”) or for 3 s at 3000 mW/cm2 (“3 s”). The samples were stored at 37 °C in distilled water and tested after 1, 6 and 12 months. The samples polymerised in the “3 s” mode had statistically similar or higher bond strength than the samples cured in “20 s” mode, except for the Tetric PowerFlow (1 month) and SDR+ (6 month). The flowable materials Tetric PowerFlow and SDR Plus initially showed the highest values in the “3 s” and “20 s” groups, which decreased after 12 months. The bond strength was statistically similar for all materials and curing protocols after 12 months, except for Tetric PowerFill cured with the “3 s” protocol (21.22 ± 5.0 MPa), which showed the highest value. Tetric PowerFill showed the highest long-term bond strength. While “3 s” curing resulted in equal or better shear bond strength, its use can only be recommended for a material with an AFCT agent such as Tetric PowerFill.