Effects of Aging Treatments on the Age Hardening Behavior and Microstructures in an Al-Mg-Si-Cu Alloy

Author:

Liu Limei1,Hou Yingpeng2,Ye Tuo2,Zhang Like2,Huang Xuan2,Gong Yuqing2,Liu Chao2,Wu Yuanzhi12,Duan Shiyun1

Affiliation:

1. Research Institute of Automobile Parts Technology, Hunan Institute of Technology, Hengyang 421002, China

2. College of Intelligent Manufacturing and Mechanical Engineering, Hunan Institute of Technology, Hengyang 421002, China

Abstract

In this study, we investigated the effects of modified aging treatments on the microstructures and hardness in a commercial 6016 Al alloy through hardness tests and transmission electron microscopy (TEM) observations. The results demonstrate that many fine needle-like β″ phases contribute to the high hardness of peak-aged (T6) alloys. Over-aging treatments lead to the precipitation of lath-like β′, β″/disordered, or B′/disordered composite phases. Moderate over-aging treatment results in the coarsening of grain boundary precipitates (GBPs) and widening of the precipitate-free zone (PFZ), while heavy over-aging treatment triggers the re-precipitation of Cu-containing GBPs and increases the number density of GBPs. A retrogression and re-aging (RRA) treatment precipitates β″, lath-like β′, and disordered phases, while a two-step aging (T78) treatment precipitates β″, B′, and disordered phases. Both the T78 and the RRA treatments lead to the coarsening of GBPs and the widening of PFZs. The decreased hardness during over-aging treatments is attributed to a combination of coarsening intragranular precipitates and/or wider PFZs. The T78 and RRA tempers achieve 95.5% and 94% of the hardness values of the T6 treatment, respectively. The hardness values of the RRA and T78 treated alloys are related to the finer nano-sized precipitates formed during the high temperature process. These precipitates can compensate for the loss of hardness caused by the increase in the widths of the PFZs and the coarsening of the matrix precipitates. The relationship between the hardness and microstructures such as PFZs and precipitates in the matrix during various heat treatments is elucidated.

Funder

National Natural Science Foundation of China

Hunan Provincial Natural Science Foundation

Hunan Provincial Science and Technology Talent Plan Project

Provincial Open Project of Applied Characteristic Discipline

Hunan Provincial Department of Education Scientific Research Project

National College Students’ Innovation and Entrepreneurship Training Program

Hunan Provincial College Students’ Innovation and Entrepreneurship

Publisher

MDPI AG

Cited by 1 articles. 订阅此论文施引文献 订阅此论文施引文献,注册后可以免费订阅5篇论文的施引文献,订阅后可以查看论文全部施引文献

同舟云学术

1.学者识别学者识别

2.学术分析学术分析

3.人才评估人才评估

"同舟云学术"是以全球学者为主线,采集、加工和组织学术论文而形成的新型学术文献查询和分析系统,可以对全球学者进行文献检索和人才价值评估。用户可以通过关注某些学科领域的顶尖人物而持续追踪该领域的学科进展和研究前沿。经过近期的数据扩容,当前同舟云学术共收录了国内外主流学术期刊6万余种,收集的期刊论文及会议论文总量共计约1.5亿篇,并以每天添加12000余篇中外论文的速度递增。我们也可以为用户提供个性化、定制化的学者数据。欢迎来电咨询!咨询电话:010-8811{复制后删除}0370

www.globalauthorid.com

TOP

Copyright © 2019-2024 北京同舟云网络信息技术有限公司
京公网安备11010802033243号  京ICP备18003416号-3