Experimental and Computational Study of Microhardness Evolution in the HAZ for Al–Cu–Li Alloys

Author:

Maritsa Stavroula1ORCID,Deligiannis Stavros2,Tsakiridis Petros E.2ORCID,Zervaki Anna D.1

Affiliation:

1. Shipbuilding Technology Laboratory, School of Naval Architecture and Marine Engineering, National Technical University of Athens, Zografou, 157 80 Athens, Greece

2. Laboratory of Physical Metallurgy, School of Mining and Metallurgical Engineering, National Technical University of Athens, Zografou, 157 80 Athens, Greece

Abstract

The Laser Beam Welding (LBW) of aluminum alloys has attracted significant interest from industrial sectors, including the shipbuilding, automotive and aeronautics industries, as it expects to contribute to significant cost reduction associated with the production of high-quality welds. To comprehend the behavior of welded structures in regard to their damage tolerance, the application of fracture mechanics serves as the instrumental tool. However, the methods employed overlook the changes in the microstructure within the Heat-Affected Zone (HAZ), which leads to the degradation of the mechanical properties of the material. The purpose of this study is to simulate microhardness evolution in the HAZ of AA2198-T351 LBW. The material represents the latest generation of Al-Cu-Li alloys, which exhibit improved mechanical properties, enhanced damage tolerance behavior, lower density and better corrosion and fatigue crack growth resistance than conventional Al-Cu alloys. In this work, the microhardness profile of LBW AA2198 was measured, and subsequently, through isothermal heat treatments on samples, the microhardness values of the HAZ were replicated. The conditions of the heat treatments (T, t) were selected in line with the thermal cycles that each area of the HAZ experienced during welding. ThermoCalc and DICTRA were employed in order to identify the strengthening precipitates and their evolution (dissolution and coarsening) during the weld thermal cycle. The microstructure of the heat-treated samples was studied employing LOM and TEM, and the strengthening precipitates and their characteristics (volume fraction and size) were defined and correlated to the calculations and the experimental conditions employed during welding. The main conclusion of this study is that it is feasible to imitate the microstructure evolution within the HAZ through the implementation of isothermal heat treatments. This implies that it is possible to fabricate samples for fatigue crack growth tests, enabling the experimental examination of the damage tolerance behavior in welded structures.

Publisher

MDPI AG

同舟云学术

1.学者识别学者识别

2.学术分析学术分析

3.人才评估人才评估

"同舟云学术"是以全球学者为主线,采集、加工和组织学术论文而形成的新型学术文献查询和分析系统,可以对全球学者进行文献检索和人才价值评估。用户可以通过关注某些学科领域的顶尖人物而持续追踪该领域的学科进展和研究前沿。经过近期的数据扩容,当前同舟云学术共收录了国内外主流学术期刊6万余种,收集的期刊论文及会议论文总量共计约1.5亿篇,并以每天添加12000余篇中外论文的速度递增。我们也可以为用户提供个性化、定制化的学者数据。欢迎来电咨询!咨询电话:010-8811{复制后删除}0370

www.globalauthorid.com

TOP

Copyright © 2019-2024 北京同舟云网络信息技术有限公司
京公网安备11010802033243号  京ICP备18003416号-3