Abstract
Localized heat sources, such as flame guns and high-energy lasers, can cause severe damage to conventional materials. In this study, a novel localized heat-resistant coating with a high in-plane thermal conductivity was designed and prepared. Reduced graphene oxide (rGO) effectively improved the in-plane thermal conductivity of the polyvinyl alcohol (PVA) film, while maintaining the thermal insulation of the resin matrix in the through-plane direction. This characteristic of the rGO/PVA film was combined with the thermal insulation of boron-modified phenolic resin (BPF), and the prepared composite coating with two layers of rGO/PVA films effectively lowered the back-surface temperature in the flame ablation test from 151 to 107 °C. In addition, the area of the ablation-affected region of coating was increased to 103.6 cm2 from 31.9 cm2, indicating an excellent heat transfer performance. The layer-by-layer structure could realize the compatibility of high in-plane thermal conductivity and good through-plane thermal insulation. The synergy of these two different characteristics is demonstrated to be the key to improving the localized heat-resistant performance of the composite coating. This study effectively expands the application range of high-conductive film, and the obtained coating could act as a shield against butane flame, high energy lasers, and other localized heat.
Funder
National Key Laboratory Foundation of Science and Technology on Materials under Shock and Impact
Natural Science Foundation of Fujian Province
Subject
Polymers and Plastics,General Chemistry
Cited by
2 articles.
订阅此论文施引文献
订阅此论文施引文献,注册后可以免费订阅5篇论文的施引文献,订阅后可以查看论文全部施引文献