Abstract
Metal corrosion is becoming increasingly serious in oil and gas production, and one way to solve this problem is to modify the metal surface. Thus, a corrosion inhibition coating on the N80 steel was constructed via the self-polymerization and assembling of the dopamine. The optimum reaction condition of polydopamine films was determined by the corrosion rate assessment of the films coated N80 steel, which was the reaction at 60 °C and 5 g/L dopamine in the Tris-HCl buffer solution (pH = 8.5) for 1 h. The spectral results confirmed the existence of the polydopamine coating on the surface of N80 steel, and high stability of the coating in the oil well produced water was observed. The anti-corrosion performance of the polydopamine-coated N80 steel confirmed that high temperature accelerated the anti-corrosion effect of the coating, and the corrosion rate of N80 plate in 90 °C oil well produced water was 0.0591 mm·a−1, lower than the standard value. The corrosion rates of the polydopamine coated N80, A3 and J55 plates at 90 °C were 0.0541 mm·a−1, 0.0498 mm·a−1 and 0.0455 mm·a−1, respectively. No significant effects of the categories of corrosive medium and steel plate on the performance of the coating were observed.
Funder
National Natural Science Foundation of China
Subject
Polymers and Plastics,General Chemistry
Reference29 articles.
1. Injection-production adjustment of typical wellgroup in companied fault-block reservoirs;Cui;Spec. Oil Gas Reserv.,2015
2. Synthesis and Properties of Octadecyl Trimethyl Ammonium Polyacrylic Surfactants
3. Investigation of aniline and N,N-dimethylaniline as acidic corrosion inhibitor: A structure-efficiency relationship study;Chen;J. Phys. Chem. B,2020
4. Synthesis of two chiral surfactants by a simple method and the surface activity evaluation
5. Synthesis and Interfacial Activity of a New Quaternary Ammonium Surfactant as an oil/gas field chemical
Cited by
8 articles.
订阅此论文施引文献
订阅此论文施引文献,注册后可以免费订阅5篇论文的施引文献,订阅后可以查看论文全部施引文献