Abstract
This study investigated the potential effect of vacuum annealing on the microstructure and hot salt corrosion behavior of CoNiCrAlY/YSZ/LaMgAl11O19 (LMA) double-ceramic coatings. A hot-salt corrosion test revealed that sprayed coatings exhibited an unsatisfactory anti-corrosion performance, and the LMA layer underwent severe fracture and corrosion degradation. Vacuum annealing induced a prominent recrystallization of the amorphous phase in LMA layer, triggering severe volume shrinkage and microcrack initiation. The recrystallization and volume shrinkage of the LMA layer were aggravated by an increase in the annealing temperature. The annealed coating with a higher fraction of the LaMA phase showed superior resistance to hot-salt corrosion. However, the salt mixture diffused simultaneously along the microcracks and eventually eroded into the YSZ layer. These results confirmed that vacuum annealing significantly enhanced the hot-salt corrosion resistance of the LMA layer. However, it deteriorated the barrier effect of the salt mixture through microcrack formation.
Funder
Southwest Institute of Technology and Engineering Cooperation fund
Subject
Materials Chemistry,Surfaces, Coatings and Films,Surfaces and Interfaces
Cited by
3 articles.
订阅此论文施引文献
订阅此论文施引文献,注册后可以免费订阅5篇论文的施引文献,订阅后可以查看论文全部施引文献