Influence of Scanning Paths on the Weld Pool Behavior, Microstructure, and Mechanical Property of AA2060 Al-Li Alloy Joints by Laser Beam Oscillation Welding

Abstract

In this paper, the laser beam oscillation welding (LBOW) was utilized to weld a 2 mm thick AA2060 aluminum-lithium (Al-Li) alloy plate. The weld pool behaviors under three scanning paths (pure laser, O-shaped, and ∞-shaped) were investigated. It was observed that the O-shaped scanning path resulted in the most stable welding process. In addition, the weld macroscopic formation, microstructure, and mechanical property between different paths were studied. The results showed that pure laser and ∞-shaped patterns produced welding defects such as spatters and collapse during the welding process, while the O-shaped pattern exhibited good macroscopic formation at varying laser powers. The O-shaped pattern promoted the finest grain in the weld center and reduced the heat input during the welding process. The equiaxed grain zone (EQZ) width of the O-shaped pattern is the smallest compared to the other two patterns at high laser power. In addition to this, the O-shaped pattern could effectively reduce the porosity in the weld. When an O-shaped scanning pattern was adopted at the ideal laser power parameter of 3000 W, the microhardness of the weld center increased by approximately 5.6% compared to pure laser mode.