Abstract
To further improve the hydrophobic and thermal properties of fluorinated polyurethane (FPU), we initially prepared the fluorine- and silicon-containing pendant groups’ diols (DEFA and DESiA) by Michael addition reaction. Next, we synthesized a series of co-modified polyurethane nanocomposite (TPFPU-SiO2) latexes by terminal and pendant fluoroalkyl segments via varying the additive amount of silica sols. Structure and performance properties of the target materials were characterized by IR, TEM, TGA, DSC, XRD, XPS, SEM, AFM, and contact angle measurements. Results showed that with the increase in silica sols dosage, the mean particle size of the TPFPU-SiO2 latexes was increased and their emulsion stability gradually decreased. The thermal stability of the TPFPU-SiO2 films were gradually increased and hydrophobicity of the TPFPU-SiO2 films increased first and then slightly decreased. The maximum water contact angle on the TPFPU-SiO2 films was 119.8° and the lowest water absorptivity was 2.49%. Thus, these novel fluorinated polyurethane nanocomposite latexes can find valuable applications in heat-resistant and anti-fouling coatings.
Funder
Natural Science Foundation of Zhejiang Province
Doctorial Research Foundation of Shaanxi University of Science and Technology
Subject
Materials Chemistry,Surfaces, Coatings and Films,Surfaces and Interfaces
Reference27 articles.
1. Characterization and application of low surface energy fluorinated polymer in leather finishing;Qin;J. Soc. Leather Technol. Chem.,2010
2. Synthesis and properties of quick-drying UV-curable hyperbranched waterborne polyurethane coating;Boton;Prog. Org. Coat.,2018
3. Preparation and application of a high temperature activated industrial gelatin wood adhesive;Wang;Fine Chem.,2020
4. Determination of vibroacoustic parameters of polyurethane mats for residential building purposes;Krzysztof;Polymers,2022
5. Lyu, J.H., Xu, K.Y., Zhang, N., Lu, C.S., Zhang, Q.F., Yu, L., Feng, F., and Li, X.N. (2019). In situ incorporation of diamino silane group into waterborne polyurethane for enhancing surface hydrophobicity of coating. Molecules, 24.