Electrochemical Characteristics and Corrosion Mechanisms of High-Strength Corrosion-Resistant Steel Reinforcement under Simulated Service Conditions

Author:

Yuan Jing12,Li Pei3,Zhang Huanhuan1,Yin Shubiao1ORCID,Xu Mingli1

Affiliation:

1. College of Metallurgy and Energy Engineering, Kunming University of Science and Technology, Kunming 650032, China

2. Xinyu Iron & Steel Group Co., Ltd., Xinyu 338001, China

3. Institute for Carbon Neutrality, University of Science and Technology Beijing, Beijing 100083, China

Abstract

Long-term steel reinforcement corrosion greatly impacts reinforced concrete structures, particularly in marine and coastal settings. Concrete failure leads to human casualties, requiring extensive demolition and maintenance, which represents an inefficient use of energy and resources. This study utilizes microscopic observation, atomic force microscopy (SKPM), electrochemical experiments, and XPS analysis to investigate the corrosion behavior of 500CE and 500E under identical conditions. We compared 500E with 500CE, supplemented with 0.94% Cr, 0.46% Mo, 0.37% Ni, and 0.51% Cu through alloying element regulation to obtain a finer ferrite grain and lower pearlitic content. The results indicate that 500CE maintains a stable potential, whereas 500E exhibits larger grain sizes and significant surface potential fluctuations, which may predispose it to corrosion. In addition, despite its more uniform microstructure and stable electrochemical activity, 500E shows inferior corrosion resistance under prolonged exposure. The electrochemical corrosion rate of 500CE in both the pristine and passivated states and for various passivation durations is slower than that of 500E, indicating superior corrosion performance. Notably, there is a significant increase in the corrosion rate of 500E after 144 h of exposure. This study provides valuable insights into the chloride corrosion phenomena of low-alloy corrosion-resistant steel reinforcement in service, potentially enhancing the longevity of reinforced concrete structures.

Publisher

MDPI AG

同舟云学术

1.学者识别学者识别

2.学术分析学术分析

3.人才评估人才评估

"同舟云学术"是以全球学者为主线,采集、加工和组织学术论文而形成的新型学术文献查询和分析系统,可以对全球学者进行文献检索和人才价值评估。用户可以通过关注某些学科领域的顶尖人物而持续追踪该领域的学科进展和研究前沿。经过近期的数据扩容,当前同舟云学术共收录了国内外主流学术期刊6万余种,收集的期刊论文及会议论文总量共计约1.5亿篇,并以每天添加12000余篇中外论文的速度递增。我们也可以为用户提供个性化、定制化的学者数据。欢迎来电咨询!咨询电话:010-8811{复制后删除}0370

www.globalauthorid.com

TOP

Copyright © 2019-2024 北京同舟云网络信息技术有限公司
京公网安备11010802033243号  京ICP备18003416号-3