Preparation of Ti-46Al-8Nb Alloy Ingots beyond Laboratory Scale Based on BaZrO3 Refractory Crucible

Abstract

The high Nb-containing TiAl-based alloy ingot beyond laboratory scale with a composition of Ti-46Al-8Nb (at.%) was prepared by a vacuum induction melting process based on a BaZrO3 refractory crucible. A round bar ingot with a diameter of 85 mm and a length of 430 mm was finally obtained, and the chemical composition, solidification pathway, microstructure and tensile properties of the ingot were investigated. The results show that the deviations of Al and Nb content along a 430 mm long central part of the ingot are approximately ±0.39 at.% and ±0.14 at.%, and the oxygen content in the ingot can be controlled at around 1000 ppm. The structure of the alloy ingot is a full lamellar structure composed of γ and α2 phases, and the thickness of the lamellae is approximately 0.53 μm. In case of the α2 phase, the surface content of the ingot is higher than the middle region and the centrical region; also, it indicated a decreasing trend. During cooling, the alloy solidified from a peritectic reaction (L + β→α) rather than the solidified via β phase (β→α). In addition to Al segregation and Nb segregation, β-phase particles associated with γ phase at the triple junction of the colonies were observed. Moreover, the tensile properties of the longitudinal-cut sample in the ingot is significantly better than those of the transverse-cut sample, with a tensile strength of up to as high as 700 MPa and a corresponding fracture elongation of 1.1%. However, the tensile strength of the transverse-cut sample is only 375 MPa, and the fracture elongation is 0.52%.