Abstract
Since the chemical composition of wood is closely related to its mechanical properties, chemical analysis techniques such as near-infrared (NIR) spectroscopy provide a reasonable non-destructive method for predicting wood strength. In this study, we used NIR spectra with principal component analysis (PCA) to reveal that vacuum hydrothermal (VH) treatment causes degradation of hemicellulose as well as the amorphous region of cellulose, resulting in lower hydroxyl and acetyl group content. These processes increase the crystallinity of the luanta fir wood (Cunninghamia konishii Hayata), which, in turn, effectively increases its compressive strength (σc,max), hardness, and modulus of elasticity (MOE). The PCA results also revealed that the primary factors affecting these properties are the hemicellulose content, hydroxyl groups in the cellulose amorphous region, the wood moisture content, and the relative lignin content. Moreover, the ratios of performance deviation (RPDs) for the σc,max, shear strength (σs,max), hardness, and modulus of rupture (MOR) models were 1.49, 1.24, 1.13, and 2.39, indicating that these models can be used for wood grading (1.0 < RPD < 2.5). Accordingly, NIR can serve as a useful tool for predicting the mechanical properties of VH-treated wood.
Funder
Ministry of Science and Technology
Subject
Polymers and Plastics,General Chemistry
Cited by
1 articles.
订阅此论文施引文献
订阅此论文施引文献,注册后可以免费订阅5篇论文的施引文献,订阅后可以查看论文全部施引文献