Effect of zirconia in the corrosion behavior of intermetallic Mo3Si alloy in molten salts mixture of NaNO3 and KNO3

Author:

Brito‐Hernádez Daniel1,Rosales‐Cadena Isaí1,Gónzalez‐Rodríguez José G.1ORCID,Uruchurtu‐Chavarín Jorge1,Guardían‐Tapia Rene1,Vera‐Dimas José G.2,López‐Sesenes Roy2ORCID

Affiliation:

1. Centro de Investigación en Ingeniería y Ciencias Aplicadas (CIICAp) Universidad Autónoma del Estado de Morelos Cuernavaca Morelos México

2. Facultad de Ciencias Químicas e Ingeniería (FCQeI) Universidad Autónoma del Estado de Morelos Cuernavaca Morelos México

Abstract

AbstractThe corrosion effect of zirconia addition, 1, 2, and 5 atomic percent (at.%), on the hot corrosion behavior of Mo3Si intermetallic alloy in 60 wt.% NaNO3 + 40 wt.% KNO3 at 600°C, has been evaluated by using electrochemical methods. Electrochemical techniques included electrochemical noise analyses (ENA), polarization curves (PC), and linear polarization resistance (LPR). The average grain size decreased when the specimen was alloyed with Zr from 90 μm for as‐cast Mo3Si, down to 25 and 10 μm for alloys containing 1, 2, and 5 at.% Zr, respectively. All specimens showed a passive behavior, with the corrosion current density values decreasing for adding either 1 or 2 at.% Zr but increasing for specimens containing 5 at.% Zr. The corrosion process was under charge transfer control for the as‐cast alloy or when 1 or 2 at.% Zr was added, but it was diffusion controlled when 5 at.% Zr was added. The noise resistance value (Rn) increased for specimens containing 1 or 2 at.% Zr but decreased when 5 at.% Zr was added. X‐ray diffraction showed the presence of SiO2, MoO4, Mo4O11, and ZrO2 in the passive layer.

Publisher

Wiley

Subject

Materials Chemistry,Metals and Alloys,Surfaces, Coatings and Films,Mechanical Engineering,Mechanics of Materials,Environmental Chemistry,Materials Chemistry,Metals and Alloys,Surfaces, Coatings and Films,Mechanical Engineering,Mechanics of Materials,Environmental Chemistry,Materials Chemistry,Metals and Alloys,Surfaces, Coatings and Films,Mechanical Engineering,Mechanics of Materials,Environmental Chemistry

Cited by 1 articles. 订阅此论文施引文献 订阅此论文施引文献,注册后可以免费订阅5篇论文的施引文献,订阅后可以查看论文全部施引文献

同舟云学术

1.学者识别学者识别

2.学术分析学术分析

3.人才评估人才评估

"同舟云学术"是以全球学者为主线,采集、加工和组织学术论文而形成的新型学术文献查询和分析系统,可以对全球学者进行文献检索和人才价值评估。用户可以通过关注某些学科领域的顶尖人物而持续追踪该领域的学科进展和研究前沿。经过近期的数据扩容,当前同舟云学术共收录了国内外主流学术期刊6万余种,收集的期刊论文及会议论文总量共计约1.5亿篇,并以每天添加12000余篇中外论文的速度递增。我们也可以为用户提供个性化、定制化的学者数据。欢迎来电咨询!咨询电话:010-8811{复制后删除}0370

www.globalauthorid.com

TOP

Copyright © 2019-2024 北京同舟云网络信息技术有限公司
京公网安备11010802033243号  京ICP备18003416号-3