Damage evaluation of carbon fiber reinforced composites under corrosion condition of sour gas well

Author:

Wujun Chen1,Zhiming Yu2ORCID,Rui Zhang1,Dezhi Zeng2ORCID,Baojun Dong3,Xi Wang2,Kunji Ming2

Affiliation:

1. Sinopec Research Institute of Petroleum Engineering, Co., Ltd Beijing China

2. State Key Laboratory of Oil & Gas Reservoir Geology and Exploitation Southwest Petroleum University Chengdu China

3. China University of Petroleum—Beijing at Karamay Karamay China

Abstract

AbstractThe paper focuses on the excellent chemical inertness characteristics of nonmetallic materials and evaluates the performance of three types of new carbon fiber‐reinforced resin‐based composites under various simulated corrosion conditions in wellbores. Through comprehensive analysis of macro and micromorphology, moisture absorption performance, strength performance, and molecular structure, the damage characteristics and applicability of carbon fiber composites in oil and gas wellbore conditions were clarified. T700/epoxy and T300/epoxy composites experienced damage dominated by physical effects such as moisture absorption and wet thermal stress, manifested as swelling, deformation, and cracking at the macro level, and pore formation and delamination cracking at the micro level. After continuous corrosion tests, the tensile strength of T700/bismaleimide composite (913 MPa) was higher than that of T700/epoxy composite (814 MPa) and T300/epoxy composite (636 MPa), with reductions of 12.4%, 14.3%, and 19.5% respectively. The research results showed T700 carbon fiber/bismaleimide resin composites had the best mechanical and chemical stability.

Publisher

Wiley

同舟云学术

1.学者识别学者识别

2.学术分析学术分析

3.人才评估人才评估

"同舟云学术"是以全球学者为主线,采集、加工和组织学术论文而形成的新型学术文献查询和分析系统,可以对全球学者进行文献检索和人才价值评估。用户可以通过关注某些学科领域的顶尖人物而持续追踪该领域的学科进展和研究前沿。经过近期的数据扩容,当前同舟云学术共收录了国内外主流学术期刊6万余种,收集的期刊论文及会议论文总量共计约1.5亿篇,并以每天添加12000余篇中外论文的速度递增。我们也可以为用户提供个性化、定制化的学者数据。欢迎来电咨询!咨询电话:010-8811{复制后删除}0370

www.globalauthorid.com

TOP

Copyright © 2019-2024 北京同舟云网络信息技术有限公司
京公网安备11010802033243号  京ICP备18003416号-3