Fatigue life improvement by shot peening for pre‐fatigue tested carburized steel

Author:

Fujino Masashi1,Tsuji Toshiya2,Takahashi Koji1ORCID

Affiliation:

1. Yokohama National University Yokohama Japan

2. Sintokogio, LTD Toyokawa Aichi Japan

Abstract

AbstractThe effect of shot peening (SP) on pre‐fatigue tested carburized steel was investigated. Plane‐bending fatigue tests were conducted on carburized CrMo steel that was pre‐fatigue tested and treated with SP. Fatigue cracks were induced by pre‐fatigue tests with a stress amplitude of σa = 1000 MPa, and the number of the pre‐fatigue test cycles was 2.0 × 104 (L5 test) and 4.0 × 104 (L15 test). We compared the fatigue lives of the fatigue‐damaged and smooth specimens without fatigue damage treated with the same SP. The fatigue life of the L5 tested specimens with SP was longer than that of the non‐fatigue damaged smooth specimens after SP. Therefore, the fatigue cracks introduced by the L5 test can be rendered harmless by SP. Furthermore, near‐surface material properties were evaluated and the mechanisms of rendering surface cracks harmless were investigated.

Publisher

Wiley

同舟云学术

1.学者识别学者识别

2.学术分析学术分析

3.人才评估人才评估

"同舟云学术"是以全球学者为主线,采集、加工和组织学术论文而形成的新型学术文献查询和分析系统,可以对全球学者进行文献检索和人才价值评估。用户可以通过关注某些学科领域的顶尖人物而持续追踪该领域的学科进展和研究前沿。经过近期的数据扩容,当前同舟云学术共收录了国内外主流学术期刊6万余种,收集的期刊论文及会议论文总量共计约1.5亿篇,并以每天添加12000余篇中外论文的速度递增。我们也可以为用户提供个性化、定制化的学者数据。欢迎来电咨询!咨询电话:010-8811{复制后删除}0370

www.globalauthorid.com

TOP

Copyright © 2019-2024 北京同舟云网络信息技术有限公司
京公网安备11010802033243号  京ICP备18003416号-3