Hot isostatic pressing as an alternative thermo‐mechanical treatment for metallic full‐arch implant‐supported frameworks obtained by additive and subtractive manufacturing technology: Vertical and horizontal fit, screw removal torque, and stress analysis

Abstract

AbstractPurposeTo assess vertical and horizontal fit, screw removal torque, and stress analysis (considered biomechanical aspects) of full‐arch implant frameworks manufactured in Ti‐6Al‐4V through milling, and additive manufacturing Direct Metal Laser Sintering (DMLS) and Electron Beam Melting (EBM), and the effect of the thermo‐mechanical treatment Hot Isostatic Pressing (HIP) as a post‐treatment after manufacturing.Material and MethodsMaxillary full‐arch implant frameworks were made by milling, DMLS, and EBM. The biomechanical assessments were screw removal torque, strain‐gauge analyses, and vertical and horizontal marginal fits. The vertical fit was assessed by the single‐screw test and with all screws tightened. All frameworks were submitted to a standardized HIP cycle (920°C, 1000 bar pressure, 2 h), and the tests were repeated (α = 0.05).ResultsAt the initial time, milled frameworks presented higher screw removal torque values, and DMLS and EBM frameworks presented lower levels of strain. Using the single‐screw test, milled and DMLS frameworks presented higher vertical fit values, and with all screws tightened and horizontally, higher fit values were found for milled frameworks, followed by DMLS and EBM. After HIP, milling and EBM frameworks presented higher screw removal torque values; the lowest strain values were found for EBM. Using the single‐screw test, milled and DMLS frameworks presented higher vertical fit values, and with all screws tightened and horizontally no differences were found.ConclusionsDMLS and EBM full‐arch frameworks presented adequate values of screw removal torque, strain, and marginal fit, although the worst values of marginal fit were found for EBM frameworks. The HIP cycle enhanced the screw removal torque of milled and EBM frameworks and reduced the strain values of milled frameworks. The HIP represents a reliable post‐treatment for Ti‐6Al‐4V dental prostheses produced by milling and EBM technologies.