Properties of tartaric acid modified steel slag as supplementing cementitious materials

Author:

Tang Panpan1,Xiong Yangkai1,Huang Lei2,Fang Zhiqiang1,Jiang Hao1,Wang Guoqing1ORCID

Affiliation:

1. School of Materials Science and Engineering Hainan University Hai Kou China

2. Chinese National Engineering Research Center for Petroleum and Natural Gas Tubular Goods Co., Ltd. Xi'an China

Abstract

AbstractBy using tartaric acid (TA) as a wet‐method modifier to modify steel slag powder (SS), it is helpful to reduce the content of free calcium oxide (f‐CaO) in SS and further improve the mechanical properties and soundness of SS as supplementing cementitious materials (SCM) in the mortar. The results indicate that with the addition of 2 wt% of TA, the number of large particles bigger than 45 µm in the SS decreased, resulting in predominantly smaller particles smaller than 45 µm. While the specific surface area increased from 417 to 704 m2/kg, the water consumption at standard consistency was significantly reduced. The soundness of the paste SS as SCM had improved including the f‐CaO content decreased from 4.81% to 0.95%, and the Le Chatelier expansion reduced from 4.5 to 1.5 mm. The mechanical properties were significantly enhanced, with the flexural strength increasing from 5.6 to 7.8 MPa, and the compressive strength rising from 38.8 to 52.7 MPa. After 28 days of curing in water, the hydration products of the mortar are hydrated calcium silicate (C‐S‐H), calcium hydroxide (CH), and calcium carbonate (CaCO3).

Funder

National Natural Science Foundation of China

Duke University

Publisher

Wiley

同舟云学术

1.学者识别学者识别

2.学术分析学术分析

3.人才评估人才评估

"同舟云学术"是以全球学者为主线,采集、加工和组织学术论文而形成的新型学术文献查询和分析系统,可以对全球学者进行文献检索和人才价值评估。用户可以通过关注某些学科领域的顶尖人物而持续追踪该领域的学科进展和研究前沿。经过近期的数据扩容,当前同舟云学术共收录了国内外主流学术期刊6万余种,收集的期刊论文及会议论文总量共计约1.5亿篇,并以每天添加12000余篇中外论文的速度递增。我们也可以为用户提供个性化、定制化的学者数据。欢迎来电咨询!咨询电话:010-8811{复制后删除}0370

www.globalauthorid.com

TOP

Copyright © 2019-2024 北京同舟云网络信息技术有限公司
京公网安备11010802033243号  京ICP备18003416号-3