Characterization of delamination behavior of unidirectional graphite/PEEK laminates using cracked lap shear (CLS) specimens-Reference-Cited by-同舟云学术

Characterization of delamination behavior of unidirectional graphite/PEEK laminates using cracked lap shear (CLS) specimens

Published:1994-01 Issue:4 Volume:29 Page:379-382
ISSN:0263-8223
Container-title:Composite Structures
language:en
Short-container-title:Composite Structures

Author:

Rhee Kyong Y.

Publisher

Elsevier BV

Subject

Civil and Structural Engineering,Ceramics and Composites

Reference12 articles.

1. An evaluation of the effects of stacking sequence and thickness on the fatigue life of quasi-isotropic graphite/epoxy laminates;Harris;ASTM, STP 864,1986

2. The characterization of edge delamination growth in laminates under fatigue loading;Poursartip;ASTM, STP 937,1987

3. Stiffness-reduction mechanisms in composite laminate;Highsmith;ASTM, STP 775,1982

4. A residual strength degradation model for competing failure modes;Whitney;ASTM, STP 813,1983

5. Factors affecting the interlaminar fracture energy of graphite/epoxy laminate;Russell;ICCM,1982

Cited by 15 articles. 订阅此论文施引文献订阅此论文施引文献，注册后可以免费订阅5篇论文的施引文献，订阅后可以查看论文全部施引文献

1. Limited strength of short fiber composites: Identification of variables affecting the critical fiber length;Journal of Composite Materials;2023-03-29

2. Mixed-mode I/II fracture criteria for adhesively-bonded pultruded GFRP/steel joint;Composite Structures;2021-01

3. Mixed-mode I/II fracture behavior for adhesively-bonded pultruded GFRP joint under four-point bending;Composite Structures;2020-11

4. Mixed mode testing of a multi-directional woven laminate;International Journal of Fracture;2020-03-16

5. Characterization of interlaminar fracture modes I, II, and I-II of carbon/epoxy composites including in-service related bonding quality conditions;Polymer Testing;2019-08