Analysis of changes in lattice parameter of a grade 91 steel during thermal ageing at 550 °C-Reference-Cited by-同舟云学术

Analysis of changes in lattice parameter of a grade 91 steel during thermal ageing at 550 °C

Published:2019-03 Issue: Volume:97 Page:43-52
ISSN:1350-6307
Container-title:Engineering Failure Analysis
language:en
Short-container-title:Engineering Failure Analysis

Author:

Fetni Seifallah^ORCID,Jhinaoui Walid,Boubahri Chokri,Montero David,Briki Jalel^ORCID

Publisher

Elsevier BV

Subject

General Engineering,General Materials Science

Reference21 articles.

1. Precipitate design for creep strengthening of 9% Cr tempered martensitic steel for ultra-supercritical power plants;Abe;J. Mater. Eng. Perform.,2008

2. Microstructural evolution during long term creep tests of 9% Cr steel grades;Cipolla,2007

3. Study of the fracture surface morphology of impact and tensile tested cast and forged, grade 91 steel at room temperature for different heat treatment regimes;Pandey;Eng. Fail. Anal.,2016

4. Evolution mechanisms of T91 steel in subcritical conditions and role of anÂ internal oxidation zone;Fetni;Oxid. Met.,2018

5. The computational design of W and Co-containing creep-resistant steels with barely coarsening laves phase and M23C6 as the strengthening precipitates;Lu;Metall. Mater. Trans. A,2014

Cited by 8 articles. 订阅此论文施引文献订阅此论文施引文献，注册后可以免费订阅5篇论文的施引文献，订阅后可以查看论文全部施引文献

1. Failure Analysis of T91 Finish Superheater Tube in 660 MW Supercritical Thermal Power Plant;Journal of Materials Engineering and Performance;2024-08-27

2. High-temperature strengthening mechanism and thermal stability of Laves phase in ferritic matrix;Materials Science and Engineering: A;2022-11

3. Autogenous laser-welded dissimilar joint of ferritic/martensitic P92 steel and Inconel 617 alloy: mechanism, microstructure, and mechanical properties;Archives of Civil and Mechanical Engineering;2022-01-10

4. Creep damage characteristics and evolution of HR3C austenitic steel during long term creep;Materials Science and Engineering: A;2022-01

5. Rupture behavior and fracture mode for Inconel 625–9% Cr steel dissimilar welded joints at high temperature;Engineering Failure Analysis;2021-07