Exploring the origins of surface cracks in forged ingots: Impurity element influence and temperature-induced formation of detrimental phases in case hardening steel-Reference-Cited by-同舟云学术

Exploring the origins of surface cracks in forged ingots: Impurity element influence and temperature-induced formation of detrimental phases in case hardening steel

Published:2023-11 Issue: Volume:153 Page:107563
ISSN:1350-6307
Container-title:Engineering Failure Analysis
language:en
Short-container-title:Engineering Failure Analysis

Author:

Nikroo Morteza,Yousefi Masoud

Publisher

Elsevier BV

Subject

General Engineering,General Materials Science

Reference48 articles.

1. Graphitization cracks in Ck45 steel clips of turbofans;Yousefi;Eng. Fail. Anal.,2021

2. An investigation of the cause of failure in a spring hose clamp;Yousefi;J. Fail. Anal. Prev.,2020

3. The effect of gradient order on impact toughness of carbon S38C axle steels with induction hardening;Zhang;Eng. Fail. Anal.,2023

4. Metallurgical investigation on failure of plain carbon steel piston rod used in hydraulic jack: Role of inclusions and surface roughness;Dhanya;Eng. Fail. Anal.,2023

5. Stress corrosion cracking failure analysis of AISI 1018 carbon steel reinforcing bars in carbonated and chloride contaminated environment;Martin;Eng. Fail. Anal.,2023

Cited by 2 articles. 订阅此论文施引文献订阅此论文施引文献，注册后可以免费订阅5篇论文的施引文献，订阅后可以查看论文全部施引文献

1. Optimization of process parameters for selective chlorination and volatilization in FeO-Cu2O-CaCl2 system;Process Safety and Environmental Protection;2024-10

2. Tempered Martensite Embrittlement of the Metallic Fastener After Austempering Heat Treatment and Coating Process Due to the Existence of Inclusion;Transactions of the Indian Institute of Metals;2023-12-07