Color Changes Associated with Sandblasting, Hydrofluoric Acid Etching, and Er:YAG Laser Irradiation of Milled Feldspathic Porcelain Laminate Veneers

Abstract

SUMMARY Objectives To evaluate color changes in milled feldspathic porcelain laminate veneers following hydrofluoric acid etching (HFA), sandblasting (SB), or Er:YAG laser irradiation (LI). Methods and Materials Disc-shaped specimens (thickness=1 mm, diameter=8 mm) were milled from feldspathic porcelain blocks (n=40). Glazed specimens were randomly assigned to four subgroups (n=10 each) according to surface treatment: negative control, HFA, SB, and LI. A layer of translucent, light-cured resin cement (thickness=0.1 mm) was then applied following silanization. The color was characterized by the L*, a*, and b* uniform color space (CIE) using a reflection spectrophotometer. CIEDE2000 (ΔE00) was calculated to determine the color difference between each surface treatment and negative control groups. Data were statistically analyzed using analysis of variance (ANOVA), Kruskal-Wallis, and Dunn-Bonferroni post hoc tests. Results There were no significant differences in CIEL* and CIEb* coordinates between negative control and all surface treatment groups (p≥0.108). The SB group demonstrated significantly lower mean CIEa* (higher greenish hue) compared to other groups (p≤0.003). HFA exhibited significantly higher CIEa* (closer to red) when compared to LI (p=0.039). LI induced the smallest overall color change compared to negative control (ΔE00=1.43 [1.07]). However, the differences in ΔE00 values were not statistically significant (p=0.648). Conclusions The tested surface treatments did not affect the lightness or the yellowness of the 1-mm-thick milled feldspathic porcelain veneers. However, sandblasting resulted in a significant increase in the greenish hue. The Er:YAG laser resulted in the closest ΔE00 (1.43) to the 50:50% perceptibility threshold (ΔE00=1.2).