Designing bi-functional Ag-CoGd0.025Er0.05Fe1.925O4 nanoarchitecture via green method

Abstract

Abstract In the current study, we developed a simple and biocompatible method for producing core–shell nanoparticles (NPs). Citrate auto combustion and green procedures were used to create core–shell Ag/CoGd0.025Er0.05Fe1.925O4 (Ag/CGEFO) sample with an average crystallite size of 26.84 nm. The prepared samples were characterized via different structural techniques, such as x-ray diffraction (XRD), Raman Spectroscopy (RS), High-Resolution Transmission Electron Microscopy, and Energy Dispersive x-ray analysis. These analyses were utilized to characterize and confirm the successful formation of the core–shell architecture. For core–shell NPs, all peaks of Ag and CGEFO ferrite are detected in the XRD, confirming the co-presence of the ferrite spinel phase and the cubic Ag phase. The magnetic hysteresis curves demonstrate typical hard ferri-magnetic behavior along with maximum magnetic saturation values up to 53.74 emu g−1 for the CGEFO sample, while an enhanced coercivity is detected for the coated sample. Moreover, the width of the hysteresis loop is increased for the Ag/CGEFO sample compared to the uncoated one. This indicates that the addition of Ag as a shell increases magneto crystalline anisotropy. Moreover, the E g of uncoated CGEFO is equal to 1.4 eV, increasing to 3.6 eV for coated ones. This implies the influence of CGEFO is diminished when the surface is coated with Ag (shell), and the reflectance of the Ag/CGEFO core–shell is nearly dependent on the reflectance of the Ag shell layer. Consequently, the Ag/CGEFO can be used as a light shielding substance.