Effect of surface treatment on bonding strength of hot rolled steel aluminum clad plate

Author:

Deng Z J,Yu C,Xiao H

Abstract

The surface of steel/aluminum clad plate was treated by 0. 3 mm steel wire brush and #180 sandpaper grinding before rolling, steel plate and aluminum plate adopt the same surface treatment. Then, it was rolled at 45% reduction rate and 450 °C rolling temperature. The rolled steel/aluminum clad plates were annealed at different times, and the steel/aluminum clad plates subjected to different surface treatments were compared for differences in bonding strength and microstructure after rolling and annealing. The surface treatment of steel wire brush formed a continuous hardened layer, and the hardened layer fragment into independent pieces during rolling. The exposed fresh steel matrix was combined with aluminum matrix to form high-strength metallurgical bonding. The surface polished with sandpaper had no obvious hardening layer, and the bonding strength after rolling was lower than that treated with wire brush. After annealing, the diffusion degree of elements at the bonding interface of clad plates subjected to different surface treatment methods increased significantly, and the bonding strength increased significantly. However, due to the oxygen concentration gradient between the steel surface hardening layer and the matrix, a new kind of iron oxide was formed between the hardening layer and the steel matrix during annealing, which connected the steel matrix and the independent hardening layer pieces, and the bonding strength increased rapidly. The research results can provide reference for the surface treatment of the hot-rolled steel/aluminum clad plate.

Publisher

IOP Publishing

Subject

General Medicine

Cited by 1 articles. 订阅此论文施引文献 订阅此论文施引文献,注册后可以免费订阅5篇论文的施引文献,订阅后可以查看论文全部施引文献

同舟云学术

1.学者识别学者识别

2.学术分析学术分析

3.人才评估人才评估

"同舟云学术"是以全球学者为主线,采集、加工和组织学术论文而形成的新型学术文献查询和分析系统,可以对全球学者进行文献检索和人才价值评估。用户可以通过关注某些学科领域的顶尖人物而持续追踪该领域的学科进展和研究前沿。经过近期的数据扩容,当前同舟云学术共收录了国内外主流学术期刊6万余种,收集的期刊论文及会议论文总量共计约1.5亿篇,并以每天添加12000余篇中外论文的速度递增。我们也可以为用户提供个性化、定制化的学者数据。欢迎来电咨询!咨询电话:010-8811{复制后删除}0370

www.globalauthorid.com

TOP

Copyright © 2019-2024 北京同舟云网络信息技术有限公司
京公网安备11010802033243号  京ICP备18003416号-3