Couple effects of multi-impact damage and CAI capability on NCF composites

Abstract

Abstract In this study, the mechanical properties of non-crimp fabric (NCF) composite laminates under low-velocity impact and compression after impact (CAI) tests were studied by Scanning electron microscopy (SEM) and Digital image correlation (DIC) techniques. The impact response under different impact times, impact angles, and impact distance is studied. Similarly, in CAI test, DIC technique is used to reveal the whole process of NCF composite compression failure, and SEM is used to reveal the microscopic failure form. The experimental results show that the impact damage process of NCF composites has strong directivity. The concrete manifestation is that the internal failure will extend along the paving direction at the failure layer. The peak load generated under 20 J impact energy is about 1/2 of that under 40 J impact energy. The impact distance is one of the important factors affecting the coupling effect of multiple impacts, and the impact angle has little effect on the internal damage extension. The proportion of internal damage area also supports the relevant view, that is, the average difference in the proportion of internal damage area under different impact distance is about 5%, while the average difference in the proportion of internal damage area under different impact angles is about 3%. During the compression process, the main failure mode is shear failure and the failure mode is brittle fracture. The oblique fracture occurs only when the oblique is 45° and the impact distance is large (50 mm). The impact angle has little effect on the residual compression performance of NCF.