Influence of pre-treatment with non-thermal atmospheric pressure plasma on bond strength of TP340 titanium-PEEK direct bonding

Abstract

AbstractDirect bonding of a TP340 titanium to PEEK by hot pressing via pre-treatment of non-thermal atmospheric pressure plasma jet has been demonstrated. The plasma irradiation effect on the bonding surface on the bond strength after hot pressing was investigated. The tensile shear strength of TP340-PEEK joined by hot pressing after plasma pre-treatment was measured by comparing specimens bonded using conventional hot pressing and those bonded using adhesives. The plasma treatment to the TP340 side resulted in the formation of TiO2, which is chemically fed to oxide formation due to the irradiation of oxygen radicals generated by the plasma, resulting in a bond strength of less than 1 MPa, similar to the bond strength of the untreated specimens. The plasma irradiation effect on the PEEK side on the bond strength of TP340-PEEK bonded samples was also investigated. The bonding strength was increased by plasma irradiation to PEEK. As the plasma irradiation time was increased, the bonding strength gradually increased to 9.2 MPa, which is about 19 times higher than the bonding strength without plasma irradiation. These results suggest that oxygen radicals in the atmospheric pressure RF plasma jet produced oxygen-containing surface functional groups on the PEEK surface, which increased the strength of the TP340-PEEK direct joining.