High performance hydroxyapatite ceramics and a triply periodic minimum surface structure fabricated by digital light processing 3D printing

Abstract

AbstractHigh performance hydroxyapatite (HA) ceramics with excellent densification and mechanical properties were successfully fabricated by digital light processing (DLP) three-dimensional (3D) printing technology. It was found that the sintering atmosphere of wet CO2 can dramatically improve the densification process and thus lead to better mechanical properties. HA ceramics with a relative density of 97.12% and a three-point bending strength of 92.4 MPa can be achieved at a sintering temperature of 1300 , which makes a solid foundation for application ℃ in bone engineering. Furthermore, a relatively high compressive strength of 4.09 MPa can be also achieved for a DLP-printed p-cell triply periodic minimum surface (TPMS) structure with a porosity of 74%, which meets the requirement of cancellous bone substitutes. A further cell proliferation test demonstrated that the sintering atmosphere of wet CO2 led to improve cell vitality after 7 days of cell culture Moreover, with the possible benefit from the bio-inspired structure, the 3D-printed TPMS structure significantly improved the cell vitality, which is crucial for early osteogenesis and osteointegration.