Author:
Wu Hanqiang,Jiang Liang,Zhong Xia,Liu Jinwei,Qin Na,Qian Linmao
Abstract
AbstractEthylenediamine with two −NH2 functional groups was used as a critical complexing agent in chemical mechanical polishing (CMP) slurries for a high carbon chromium GCr15 bearing steel (equivalent to AISI 52100). The polishing performance and corresponding mechanism of −NH2 functional groups were thoroughly investigated as a function of pH. It is revealed that, when polished with ethylenediamine and H2O2-based slurries, the material removal rate (MRR) and surface roughness Ra of GCr15 steel gradually decrease as pH increases. Compared with acidic pH of 4.0, at alkaline pH of 10.0, the surface film of GCr15 steel has much higher corrosion resistance and wear resistance, and thus the material removal caused by the pure corrosion and corrosion-enhanced wear are greatly inhibited, resulting in much lower MRR and Ra. Moreover, it is confirmed that a more protective composite film, consisting of more Fe3+ hydroxides/oxyhydroxides and complex compounds with −NH2 functional groups of ethylenediamine, can be formed at pH of 10.0. Additionally, the polishing performance of pure iron and a medium carbon 45 steel exhibits a similar trend as GCr15 steel. The findings suggest that acidic pH could be feasible for amine groups-based complexing agents to achieve efficient CMP of iron-based metals.
Publisher
Springer Science and Business Media LLC
Subject
Surfaces, Coatings and Films,Mechanical Engineering
Reference54 articles.
1. Yin F, Hua L, Mao H, Han X. Constitutive modeling for flow behavior of GCr15 steel under hot compression experiments. Mater Design 43: 393–401 (2013)
2. Bhadeshia H K D H. Steels for bearings. Prog Mater Sci 57(2): 268–435 (2012)
3. Mohd Yusof N F, Ripin Z M. Analysis of surface parameters and vibration of roller bearing. Tribol T 57(4): 715–729 (2014)
4. Takabi J, Khonsari M M. On the dynamic performance of roller bearings operating under low rotational speeds with consideration of surface roughness. Tribol Int 86: 62–71 (2015)
5. Komata H, Iwanaga Y, Ueda T, Ueda K, Mitamura N. Enhanced performance of rolling bearings by improving the resistance of rolling elements to surface degradation. In Bearing Steel Technologies: 10th Volume, Advances in Steel Technologies for Rolling Bearings. Beswick J M, Edn. West Conshohocken, PA: ASTM International, 2015: 272–290.
Cited by
20 articles.
订阅此论文施引文献
订阅此论文施引文献,注册后可以免费订阅5篇论文的施引文献,订阅后可以查看论文全部施引文献