Properties of 13KhMF steel after operation and degradation under the laboratory conditions-Reference-Cited by-同舟云学术

Properties of 13KhMF steel after operation and degradation under the laboratory conditions

Published:2010-12 Issue:3 Volume:46 Page:357-364
ISSN:1068-820X
Container-title:Materials Science
language:en
Short-container-title:Mater Sci

Author:

Dzioba I. R.

Publisher

Springer Science and Business Media LLC

Subject

Mechanical Engineering,Mechanics of Materials,Condensed Matter Physics,General Materials Science

Link

http://link.springer.com/content/pdf/10.1007/s11003-010-9297-x.pdf

Reference27 articles.

1. E. I. Krutasova, Reliability of the Metal of Power-Generating Plants [in Russian], Énergoizdat, Moscow (1981).

2. V. A. Nakhalov, Reliability of Pipe Bends in Thermal Power Plants [in Russian], Énergoatomizdat, Moscow (1983).

3. T. G. Berezina, N. V. Bugai, and I. N. Trunin, Diagnostics and Prediction of the Durability of the Metal of Thermal Power Plants [in Russian], Tekhnika, Kiev (1991).

4. A. Hernas and J. Dobrzański, Trwałość i Niszczenie Elementów Kotłów i Turbin Parowych, WPŚ, Gliwice (2003).

5. A. Hernas, Żarowytrzymałość stali i stopów, WPŚ, Gliwice (2000).

Cited by 25 articles. 订阅此论文施引文献订阅此论文施引文献，注册后可以免费订阅5篇论文的施引文献，订阅后可以查看论文全部施引文献

1. Structural aspects of the degradation of the bend stretched zone;Procedia Structural Integrity;2024

2. The Structural-Mechanical State of 12Kh1MF Steel of TPP Pipeline Bend after Long-Term Operation;Materials Science;2023-11

3. Substantiation of the critical structural and mechanical state of low-alloy heat-resistant steel from steam pipelines of thermal power plant;Engineering Failure Analysis;2023-08

4. Establishing the causes of premature damage of steam turbine rotor blades of TPP;Scientific journal of the Ternopil national technical university;2023

5. Identification of the Fracture Process in Gas Pipeline Steel Based on the Analysis of AE Signals;Materials;2022-04-04